| Form of product | 50g/capsule, can be put into the cooper melt together with the sealing aluminum capsule packing while being used. |
| Consumption | 150 grams capsule for each 1metric ton of melted brass or melted alloy |
| Alloy requirements | ◆ Suitable for all copper alloy, including pure copper (99.85%) |
| ◆ Work best on brass alloy |
| ◆ Can be used to lower the casting temperatures and increase the castability and fluidity of the aluminum bronze, red brass and tin bronze. |
| ◆ Also proper for aluminum high pressure casting, parts will come out bright and shiny |
| Alloy Class and General Parameters | Dosage | Expected Results | Special Instructions |
| Grain Refinement | Deoxy-dation | Reduced Casting Temp. |
| Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb less than 0.5%.) | 150 grams per metric ton (5 grams per 100 lb.) | YES | YES | YES | Grain refinement occurs when copper content is between 57 and 63 percent. Optimal grain refinement occurs when copper content is 59.5 percent and aluminum content is 0.6 percent. See Notes 1 and 2. |
| Leaded Yellow Brass (Over 17% Zn. Sn less than 6%. Under 2% total Al, Mn. Ni, Fe, Si. Pb more than 0.5%.) | 150 grams per metric ton (5 grams per 100 lb.) | YES | YES | YES |
| High Strength Yellow Brass (Manganese Bronze) (Over 17% Zn. Over 2% total Al, Mn. Sn, Ni, Fe. Si less than 0.5%. Pb less than 0.5%. Sn less than 6%) | 50 grams per metric ton (5 grams per 100 lb.) | May reduce grain if Sn + Fe is less than 0.5% | YES | YES | |
Red Brass (2% to 8% Zn. Sn less than Zn. Pb under 0.5%) | 200 grams per metric ton (9 grams per 100 lb.) | NO | YES | YES | Use without AL tubes. Add to transfer ladle along with phos copper. If high oxygen occurs, add Mn before adding DesofinTM. |
Aluminum Bronze (Al 5% to 15%. Fe up to 10% - with or without Mn or Ni. Si less than 0.5%) | 200 grams per metric ton (18 grams per 100 lb.) | NO | YES | YES | If high oxygen occurs, add Mn before adding DesofinTM. |
Tin Bronze (Sn 2% to 20%. Zn less than Sn. Pb under 0.5%) | 200 grams per metric ton (9 grams per 100 lb.) | NO | YES | YES | Use without Al tubes. Add to transfer ladle along with phos copper |
| Notes: 1. If Sn + Fe is greater than 0.5%, intermetallic compounds will form that will leave "comet tails" when casting is polished. 2. Miller & Englehardt Co., lltd recommends use of "B-2" yellow brass alloy with DesofinTM for permanent molding applications. B[1]2 alloy composition: Cu 59.5 to 61.5%; Pb 0% to 3.0%; Al 0.5% to 0.7%, Ni 1%; Sn + Fe 0.5 % max, Mn 0.02% max, Si 0.02% max, Zn balance. |
Form of product :50g/capsule
Applied for B2 alloy
Melting method, by dipping in the copper bath
The final perfect brass-cup